MXD6 Polyadipyl-m-benzoylamine, abbreviated as mxd6, resin has higher mechanical strength and modulus than other engineering plastics, is also a special high barrier nylon material. Although the barrier of mxd6 is slightly worse than that of pvdc and evoh, its barrier is not affected by temperature and humidity, which is especially suitable for high temperature and humid occasions. In today's barrier packaging and plastic instead of steel general trend, nylon mxd6 has become one of the most eye-catching new plastic varieties. Structure performance: MXD6 nylon material has high strength, high rigidity, high thermal deformation temperature, small thermal expansion coefficient; Dimensional stability, low water absorption rate and small size change after water absorption, mechanical strength changes less; Forming shrinkage is small, suitable for precision forming processing; Excellent coating performance, especially suitable for high temperature surface coating; Excellent barrier to oxygen, carbon dioxide and other gases. Excellent mechanical and thermal properties and high strength, high modulus and heat resistance, high barrier, excellent cooking resistance. MXD6-LGF MXD6 can be compounded with glass fiber for use in fiberglass reinforced materials containing 50-60% glass fiber for exceptional strength and stiffness. Even when filled with high glass content, its smooth, resin-rich surface produces a fibre-free high gloss surface, ideal for painting, metal-plating, or creating naturally reflective shells. 1, suitable for high liquidity of thin wall It is a very fluid resin that can easily fill thin walls as thin as 0.5 mm thick even when the glass fiber content is as high as 60%. 2. Excellent surface finish A resin-rich perfect surface has a highly polished appearance, even with a high glass fiber content. 3. High strength and stiffness The tensile and flexural strength of MXD6 is similar to that of many cast metals and alloys with the addition of 50-60% glass fiber reinforced material. 4, good dimensional stability At ambient temperatures, the linear expansion coefficient (CLTE) of MXD6 glass fiber composites is similar to that of many cast metals and alloys. Strong reproducibility due to low shrinkage and the ability to maintain tight tolerances (length tolerances as low as ± 0.05% if properly formed). MXD6 replaces metal to produce high-quality structural parts for automobiles, electronics and electrical appliances In automobile parts, many occasions require material products with high mechanical strength and good oil resistance, and can be used in the range of 120 ~ 160℃ for a long time. Glass fiber reinforced MXD6 heat resistant temperature up to 225℃, high rate of strength retention at high temperature, can be used in the cylinder block, cylinder head, piston, synchronous gear, etc. MXD6/PPO alloy has high temperature resistance, high strength, oil resistance, wear resistance, good dimensional stability and other properties, can be used for the vertical outer plate of the automobile body, front and rear fenders, wheel covers and almost can not use steel plate stamping forming curved parts and automobile chassis. Datasheet for reference Application fileds Production process Xiamen LFT composite plastic Co., Ltd س: كيف يتم اختيار محتوى الألياف للمنتج؟ هل المنتج الأكبر مناسب لمواد ذات محتوى ألياف أعلى؟ ج: هذا ليس مطلقا. محتوى الألياف الزجاجية ليس أكثر هو الأفضل. المحتوى المناسب هو فقط لتلبية متطلبات كل منتج. س: في أي ظروف يمكن أن تحل الألياف الطويلة محل الألياف القصيرة؟ ما هي المواد البديلة الشائعة؟ يمكن استبدال مواد الألياف الأساسية التقليدية بألياف زجاجية طويلة ومواد LFT طويلة من ألياف الكربون في حالة العملاء الذين لا يمكن تلبية خواصهم الميكانيكية أو عندما تكون البدائل المعدنية الأعلى مطلوبة. على سبيل المثال ، غالبًا ما تحل الألياف الزجاجية الطويلة PP محل الألياف الزجاجية المقواة بالنايلون ، والألياف الزجاجية الطويلة من النايلون تحل محل سلسلة PPS. س: هل للألياف الزجاجية الطويلة وحقن ألياف الكربون الطويلة متطلبات خاصة لآلات التشكيل بالحقن والقوالب؟ ج: هناك بالتأكيد متطلبات. خاصةً من هيكل تصميم المنتج ، وكذلك فوهة اللولب لآلة التشكيل بالحقن وعملية التشكيل بالحقن لهيكل القالب يجب أن تأخذ في الاعتبار متطلبات الألياف الطويلة.

MXD6 Nylon - MXD6 is a kind of crystalline polyamide resin, which is synthesized by the condensation of m-benzoylamine and adipic acid. The advantages of nylon MXD6 1. in a wide range of temperature, maintain high strength, high rigidity 2. High thermal deformation temperature and small thermal expansion coefficient 3. Low water absorption rate, small size change after water absorption, less mechanical strength reduction 4. forming shrinkage rate is very small, suitable for precision forming processing 5. excellent coating, especially suitable for high temperature surface coating 6. oxygen, carbon dioxide and other gases also have excellent barrier Application of MXD6 in plastic modification industry MXD6 can be combined with fiberglass, carbon fiber, mineral, and/or advanced fillers for use in fiberglass reinforced materials containing 50-60% and for exceptional strength and stiffness. Even when filled with high glass content, its smooth, resin-rich surface produces a fibre-free high gloss surface, ideal for painting, metal-plating, or creating naturally reflective shells. 1. suitable for high liquidity of thin wall It is a very fluid resin that can easily fill thin walls as thin as 0.5 mm thick even when the glass fiber content is as high as 60%. 2. Excellent surface finish A resin-rich perfect surface has a highly polished appearance, even with a high glass fiber content. 3. High strength and stiffness إن قوة الشد والانثناء لـ MXD6 مماثلة لتلك الموجودة في العديد من المعادن والسبائك المصبوبة مع إضافة 50-60٪ مادة مقواة بالألياف الزجاجية. 4. ثبات أبعاد جيد في درجات الحرارة المحيطة ، يكون معامل التمدد الخطي (CLTE) لمركبات الألياف الزجاجية MXD6 مشابهًا للعديد من المعادن والسبائك المصبوبة. قابلية استنساخ قوية بسبب الانكماش المنخفض والقدرة على الحفاظ على التفاوتات الشديدة (تفاوتات الطول منخفضة تصل إلى ± 0.05٪ إذا تم تشكيلها بشكل صحيح). ورقة البيانات تم اختباره من قبل معملنا الخاص ، كمرجع فقط. أسئلة مكررة 1. كيفية اختيار محتوى الألياف للمنتج؟ هل المنتج الأكبر مناسب لمواد ذات محتوى ألياف أعلى؟ ج: هذا ليس مطلقا. محتوى الألياف الزجاجية ليس أكثر هو الأفضل. المحتوى المناسب هو فقط لتلبية متطلبات كل منتج. 2. هل يمكن تصنيع المنتجات التي تتطلب مظهرًا من مواد طويلة الألياف؟ الميزة الرئيسية للألياف الزجاجية الطويلة اللدائن الحرارية LFT-G وألياف الكربون الطويلة هي إظهار الخصائص الميكانيكية. إذا كان لدى العميل متطلبات ساطعة أو متطلبات أخرى لمظهر المنتجات ، فيجب تقييمها بالاقتران مع منتجات محددة. 3. هل هناك أي متطلبات عملية خاصة لمنتجات القولبة بالحقن بألياف الكربون الطويلة؟ يجب علينا مراعاة متطلبات الألياف الطويلة للفوهة اللولبية لآلة التشكيل بالحقن وهيكل القالب وعملية التشكيل بالحقن. تعد الألياف الطويلة مادة عالية التكلفة نسبيًا ، وتحتاج إلى تقييم مشكلة أداء التكلفة في عملية الاختيار. 

ما هو MXD6؟ من السهل معالجة النايلون الأليفاتي التقليدي ولكنه يتمتع بامتصاص قوي للماء ودرجة حرارة منخفضة لتحويل الزجاج. على الرغم من أن النايلون العطري بالكامل قد حل أوجه القصور في المنتجات الأليفاتية إلى حد كبير ، فقد زادت صعوبة المعالجة بشكل كبير. بعد عام 1972 ، صنعت Toyo Textile و Mitsubishi Gas Chemical نوعًا جديدًا من النايلون MXD6 شبه العطري ، والذي لم يتغلب فقط على عيوب الراتنجات الأليفاتية والعطرية بالكامل إلى حد كبير ، ولكن كان له أيضًا بعض مزايا الراتنجات العطرية بالكامل. يستخدم على نطاق واسع في مواد التعبئة والتغليف ذات حاجز الغاز العالي والمواد الإنشائية الهندسية. باختصار ، تتميز MXD6 بالمزايا التالية: قوة عالية ومعامل مرن ؛ درجة حرارة التزجج العالية هي 237 ℃ لـ Tm و 85 لـ Tg. انخفاض امتصاص الماء ونفاذية الرطوبة ؛ سرعة تبلور سريعة ، سهلة التشكيل والتصنيع ؛ أداء ممتاز لحاجز الغاز. لماذا تضيف ألياف زجاجية طويلة؟ يمكن للمركب المقوى بالألياف الزجاجية الطويلة أن يحل مشاكلك عندما لا توفر الطرق الأخرى للبلاستيك المقوى الأداء الذي تحتاجه أو إذا كنت ترغب في استبدال الماتال بالبلاستيك. يمكن للمركبات المقواة بالألياف الزجاجية الطويلة أن تقلل تكلفة البضائع بشكل فعال من حيث التكلفة وتحسن بشكل فعال الخصائص الميكانيكية لشبكة الهيكل العظمي الداخلية الهندسية. يتم الحفاظ على الأداء في مجموعة واسعة من البيئات. أداء MXD6 والتطبيق بالمقارنة مع المواد الأخرى ، تتميز MXD6 بمزايا القوة العالية ومعامل المرونة ، ودرجة حرارة انتقال الزجاج العالية ، وامتصاص الماء المنخفض ونفاذية الرطوبة ، وسرعة التبلور السريعة ، والقولبة والتصنيع المريحين ، وخصائص ممتازة لحاجز الغاز ، ويمكن أن تكون أيضًا حاجزًا جيدًا أمام ثاني أكسيد الكربون والأكسجين حتى في ظل الرطوبة العالية. في السوق النهائي ، نادرًا ما يتم استخدام MXD6 بمفرده ويتم إضافته عمومًا إلى بوليمرات أخرى كمكون معدل. تُستخدم المواد التي تحتوي على MXD6 بشكل أساسي في مجالات السيارات والتعبئة. بصفتها مادة بلاستيكية هندسية ، يمكن أن تحل MXD6 محل استخدام المواد المعدنية في صناعة السيارات ، مثل أدوات الطاقة ، والمواد المغناطيسية ، وغطاء السيارة ، والهيكل ، والعوارض ، وملحقات المحرك ، وما إلى ذلك. سوف نقدم لك: 1) المعلمات التقنية للمواد LFT & LFRT والتصميم الرائد ؛ 2) تصميم الجبهة والتوصيات ； 3) تقديم الدعم الفني مثل القولبة بالحقن والقولبة بالبثق. شهادة النظام شهادة نظام إدارة الجودة ISO9001 / 1949 شهادة اعتماد المختبرات الوطنية مؤسسة ابتكار البلاستيك المعدلة شهادة فخرية اختبار REACH & ROHS للمعادن الثقيلة

MXD6 الراتنج سعر المصنع mxd6 حبيبات الكريات أي واحد مصنوع في مصنع بنفسي.

تعديل mxd6 هو نوع من مادة النايلون ارتفاع في درجة الحرارة المعدلة.

MXD6 التعديل هو نوع من ارتفاع في درجة الحرارة النايلون المواد المعدلة.